Home / Products / Nickel Alloys / Nickel 200 / ASTM B160 Nickel 201 Rods
Nickel 200 and Nickel 201 are solid solution strengthened, commercially pure wrought materials with good mechanical properties over a wide range of temperatures and excellent resistance to many corrosives, in particular hydroxides. Nickel 201 was a modification of 200 to control carbon (.02 max) which keeps it from being embrittled by intergranular precipitates at temperatures of 600° F to 1400° F in many processes. Typically, the elemental restrictions of both, nickel 200 and nickel 201, are combined into one, dual-certified chemistry resulting in a single alloy with the desired characteristics of both alloys, Nickel 200/201.
ASTM B160 Nickel 201 Rods
Specifications
| Standards |
Designation |
| ASTM |
B 160 |
| ASME |
160 |
| Standard |
Nickel 200 |
Nickel 201 |
| UNS |
N02200 |
N02201 |
| Werkstoff Nr. |
2.4066 |
2.4068 |
| Sizes |
Availability |
| 6mm |
|
| 8mm |
|
| 10mm |
|
| 12mm |
|
| 13mm |
|
| 16mm |
|
| 19mm |
|
| 22mm |
|
| 28mm |
|
| 40mm |
|
| 60mm |
|
| 75mm |
|
| 90mm |
|
| 120mm |
|
Dimensions
Nickel 201 Chemical Composition
|
Nickel 200 |
Nickel 201 |
| Ni |
99.0 min |
99.0 min |
| Fe |
0.4 max |
0.4 max |
| C |
0.15 max |
0.02 max |
| Mn |
0.35 max |
0.35 max |
| Si |
0.1 max |
0.2 max |
| Cu |
0.25 max |
0.25 max |
| Mg |
|
0.15 max |
| Ti |
|
0.1 max |
| S |
0.01 max |
0.01 max |
Nickel 201 Mechanical & Physical Properties
| Density |
8.9 g/cm3 |
| Melting Point |
1446 °C (2635 °F) |
| Tensile Strength |
Psi – 67000 , MPa – 462 |
| Yield Strength (0.2%Offset) |
Psi – 21500 , MPa – 148 |
| Elongation |
45 % |
Main Export Market
- Eastern Europe
- North America
- Mid East/Africa
- Central/South America
- Asia
- Western Europe
- Australasia
- UAE
Sales Locations
U.A.E,
Oman,
Saudi Arabia,
Qatar,
Bahrain,
Egypt,
Turkey
Singapore,
Thailand,
Malaysia
Indonesia
Poland
Italy
Portugal
Spain
Brazil
Chile
Venezuela
Costa Rica
USA
Canada
Angola
Sri Lanka
Russia
|
| |
|
|